dc.description.abstract |
This study was focused on the electrical conductivity for the combination of polypyrrole and
chlorophyll thin films on indium tin oxide (ITO) substrate in the bulk heterojunction solar
cell. The combination of polypyrrole and chlorophyll thin films with ratio 1:1, 1:5, 1:10, 5:1
and 10: 1 was deposited on the ITO substrate by using the Langmuir Blodgett with different
layers. The current and voltage of the thin films were measured by using four point probes
under dark and different light intensity which 10, 30, 50, 80 and 100 wm·
2
• The result of this
work showed the combination of polypyrrole and chlorophyll thin film in different ratio
successful layered on the ITO substrate with different layers. The electrical conductivity under
dark was measured by using four point probes. Four point probes with pyronometer and data
logger was used to measure the electrical conductivity under different intensity of light. The
electrical conductivity under dark was increased with the increasing number of layers
combination of polypyrrole and chlorophyll. The electrical conductivity under different light
intensity was increased with increasing the light intensity. The electrical conductivity under
different intensity of light was increase with increasing the combination polypyrrole and
chlorophyll with different ratios. As a conclusion, the 1: 10 layers of polypyrrole and
chlorophyll thin film thin films are suitable combination to increase the electrical conductivity
which is 0.2 sm·
1
at ratio 15 layers. |